In this work, the perovskite solar cells (PSCs) were fabricated with the bandgap-tunable (FA)x(MA)1-xPbI3 absorber layers through a facile two-stage deposition route. The doping was realized by adding the formamidinium iodide (FAI) into a precursor MAI solution. Both the surface morphology and electrochemical impedance spectra (EIS) were con-ducted to evaluate the absorber layers or solar cells. After the optimization, the best PSC performance of 14.73% was achieved at a nominal FAI content of 12.5 at.%. The performance enhancement was attributed to both the enhance-ment of visible light harvesting and carrier transport capability. Besides, the stability of a PSC device based on the single MAPbI3 absorber layer was also investigated, and a power conversion efficiency (PCE) of 11.27 % remained even after laying in vacuum for 10 days.