Abstract
Nowadays, compare to light crude oils, the production of heavy and extra-heavy crude oils is increasing[
Dealumination[
Besides these methods, “steam-assisted conversion (SAC)” procedure[
However, up to now, no report has approached the synthesis of sphere-like hierarchical Y zeolite consisting of primary nanosized FAU zeolite crystals. In the present work, dried gel, the precursors yielding Y, was subjected to a vapor treatment, and sphere-like hierarchical Y zeolite aggregate was therefore synthesized by SAC procedure without assistance of any organic templates or secondary mesoporogen. The effects of chemical composition like SiO2/Al2O3 in gel precursor on the formation of the sphere-like hierarchical Y zeolite were investigated and discussed in details; formation mechanism of the sphere-like hierarchical Y including hollow sphere-like Y zeolite polycrystalline aggregates was proposed on base of the results of FT-IR, 29Si NMR, SEM and TEM.
1 Experimental
1.1 Synthesis
Precursor solution yielding Y zeolite was prepared with a mole composition as following: 3.53Na2O : (4.14- 8.28)SiO2 : 1Al2O3 : (212-239)H2O. Typically, by mixing 10.2 g NaAlO2, 8.0 g NaOH, and 88 mL H2O, and stirring for giving a clear solution. Then 16-32 mL colloidal silica was added into the solution followed by stirring for 2 h. The achieved Sol-Gel mixture was divided into two parts, and marked as “A” and “B”, respectively.
The synthesis of hierarchical Y zeolite was as following: the corresponding gel “A” was transferred into a polytetrafluoroethylene cup and kept at 60 ℃ for 24 h for giving a dried gel, and the obtained dried gel was named as YP-x, here, “x” stands for SiO2/Al2O3 ratio. 2 g of the abovementioned YP-x was added to a 50 mL polytetrafluoroethylene cup, and the cup was put into an autoclave without any additional water or other solvent for crystallization at 90 ℃ for 24 h. The final product was collected by washing to neutral with water, drying in air at 110 ℃, and denoted as YS-x.
Y zeolite prepared by a traditional hydrothermal procedure was described as following: the corresponding gel “B” was transferred into an autoclave and kept at 90 ℃ for 24 h under autogenous pressure. The product was collected by filtration, washed with distilled water, dried in air, and was denoted as YH-x.
1.2 Characterization
X-ray powder diffraction (XRD) patterns were recorded using a SHIMADZU XRD-6000 X-ray diffractometer, Ni-filtered Cu Kα radiation, 40 kV and 30 mA. Framework infrared spectra of the calcined samples were obtained on a SHIMADZU FTIR-8400 spectrometer in KBr pellets. Crystal sizes and morphology of the as-synthesized samples were investigated on a JEOL JEM- 2010 transmission electron microscopy (TEM) and a HITACHI S4800 scanning electron microscopy coupled with energy dispersive spectroscopy (EDS). 29Si MAS NMR spectra were recorded on a Bruker Avance III 500 spectrometer at resonance frequencies of 99.361 MHz, 50 kHz sample spinning rate, 0.22 μs pulse width, 4 s recycle delay, and 1024 sampling frequency. N2 adsorption at 77 K was performed in a Micromeritics ASAP2400 gas sorption analyzer to study micro- and mesoporosity in the zeolite crystals. The mesopore size distribution was calculated using Barret-Joyner-Halenda (BJH) pore size model applied to the adsorption branch of the isotherm. The microporous structure was obtained from the t-plot analysis of the adsorption branch of the isotherm.
2 Results and discussion
It can be seen from Fig. 1 that after treated by vapor at 90 ℃ for 24 h, the dried gel precursors with SiO2/Al2O3 ratios of 4.14-7.25 have been transferred into pure phase Y zeolite with different crystallinity. While XRD patterns of the sample YH-5.18, which is obtained via the traditional hydrothermal crystallization from a precursor with the same chemical component as that yielding the sample YS-5.18, not only exhibits the characteristic diffraction peaks ascribed to the FAU topological structure at 2θ= 6.16°, 10.08°, 15.72°, 20.43°, and 23.67°, but also displays P zeolite characteristic diffraction peaks at 2θ= 12.46°, 17.66°, 21.67°, 30.84°. The result indicates that the different synthesis procedures affect the formation of the final products.
Figure 1.Schematic representation of the process for the formation of the sphere-like hierarchical Y zeolite composed of the loosely aggregating nanocrystallites
As shown in Fig. 2(a-b), the dried gel YP-5.18 exhibits a worm-like morphology, implying the sample an amorphous phase. After being subjected to vapor treatment at 90 ℃ for 24 h, the worm-like amorphous phase has disappeared and the dried gel has been transferred into crystalline phase (Fig. 2(e-f)). It can be seen from Fig. 2(c-j) that the crystals in all of the final products, such as YS-4.14, YS-5.18, YS-6.21, and YS-7.25, display about 1 μm sphere-like polycrystalline aggregates consisting of loosely aggregating primary crystallites with a size of about 50-300 nm. It can be seen from Fig. 2(d, f, j, i) that the increased Si/Al ratio in the precursors leads to the smaller primary crystals. The weakened characteristic peaks with increased Si/Al ratio in the precursors (Fig. 1) can therefore be partially ascribed to the decreased crystalline size of the primary crystals in the as-synthesized sphere-like Y zeolite polycrystalline aggregates. Higher Si/Al ratio of 8.28 in the precursor gives the final product YS-8.28 the similar worm-like morphology as one of dried gel YP-5.18 (Fig. 2(a-b)). While, as shown in Fig. 3(a-d), a trace of sphere-like polycrystalline aggregate composed of the primary particles with a size of about 100-300 nm can also be observed, indicating that the excessively increased Si/Al ratio in dried gel, for example YP-8.28, mainly yields the amorphous phase, which is in agreement with the result observed by XRD patterns as shown in Fig. 1.
Figure 2.SEM images of the as-synthesized YS-
(a, b) YP-5.18; (c, d) YS-4.14; (e, f) YS-5.18; (g, h) YS-6.21; (i, j) YS-7.25; (k, l) YS-8.28
Figure 3.SEM images of the as-synthesized Y zeolite yielding from the gel precursor with different Si/Al ratio
(a-d) YS-8.28; (e-g) YS-6.21; (h) YS-5.18; (i) YH-5.18
As shown in Fig. 3(i), most of the crystals in the reference sample YH-5.18 obtained by a traditional hydrothermal synthesis procedure are dense and smooth faujasite with a size of ~1000 nm, and some impure crystals, which can be ascribed to P zeolite (Fig. 1), are also observed. A large number of crystals with regular hexagonal platy shape (Fig. 3(e-g)) with size ranging from 1 to 3 μm are found in sample YS-6.21 (Fig. 3(e-g)), and a small quantity of crystals with similar hexagonal platy shape as the one in YH-6.21 can also be observed in sample YS-5.18 as shown in Fig. 3(h).
As shown in Fig. 4, TEM image of the sample YS-5.18 further discovers that the crystals in the samples prepared by the SAC procedure are the polycrystalline aggregates which are composed of loosely aggregating primary crystals with a size of about 50-300 nm, and the polycrystalline aggregates are sticky to each other. Direct evidence for the presence of meso- and macropores with a size of 10-100 nm in diameter is also provided by the TEM image as shown in Fig. 4(a) (red arrow). TEM image (Fig. 4(b)) and the corresponding reversed-phase TEM image (Fig. 4(c)) of the crystal in sample YS-5.18 suggest that some of the sphere-like polycrystalline aggregates are hollow.
Figure 4.TEM image of YS-5.18 (a), TEM image (b) and the corresponding reversed-phase TEM image (c)
FT-IR spectra of the dried gel YP-x (dotted line) and the as-synthesized YS-x (full line) are shown in Fig. 5. The characteristic vibration bands attributed to zeolite can be observed, although they are not completely identical. The bands at ~ 457 cm-1, ~570 cm-1, and ~764 cm-1 are respectively assigned to the O-T (Si or Al) bending vibrations, the double ring external linkage vibrations, and the external linkage symmetrical stretching vibrations.
Figure 5.FT-IR spectra of the samples
(a) YS-
For Y zeolite, the band at around 1010-1025 cm-1 is ascribed to the internal tetrahedral asymmetrical stretching vibration. The vibration bands between 1000 cm-1 and 1100 cm-1 are often used to identify the Si/Al ratio of zeolite framework. The anti-symmetric stretching vibration bands corresponding to YS-4.14, YS-5.18, YS- 6.21, and YS-7.25 are respectively located at 1010, 1010, 1018 and 1025 cm-1, implying the as-synthesized samples may have an increased framework Si/Al ratio[
Figure 6.SEM images and EDS analysis of the as-synthesized Y zeolite yielding from gel precursor with different Si/Al ratio
(a) YS-4.14; (b) YS-5.18; (c) YS-6.21; (d) YS-7.25
Figure 7(a) and (b) are 29Si MAS NMR spectra of sample YS-5.18 and the corresponding dried gel YP-5.18, respectively. The resonances at δ= -108 ~ -105 are assigned to Si (4Si, 0Al) sites, and those δ= -105~ -95 are assigned to Si (3Si, 1Al) sites; moreover, those at δ= -95 ~ -92, -92 ~ -86, and -86 ~ -80, are respectively assigned to the Si (2Si, 2Al), Si (1Si, 3Al), and Si (0Si, 4Al)[
Figure 7.29Si MAS NMR spectra
(a) YS-5.18; (b) YP-5.18
The building units or crystallites with the primary zeolite framework yielded during the preparation of the dried gel play an important role in the formation of the hierarchical sphere-like Y zeolite consisting of nanocrystals. The formed building units or the primary crystallites in the dried gel not only offers the target product a fast nucleation, but also plays a key role in guaranteeing the precursor to be transferred into the pure phase FAU zeolites structure. During SAC procedure, these building units or crystallite with primary zeolite framework in the dried gel induced a burst in nucleation rate[
Indeed, despite very complex for the mechanisms of zeolite growth and nucleation, it is very obvious that a high ratio of nucleation relative to growth is in favor of the formation of nanocrystals. The crystallization mechanism of the sphere-like Y consisting of loosely aggregating nanocrystallites is interpreted in Scheme 1. During preparation of dried gel, primary or/and secondary building units[
Figure 8.N2 adsorption-desorption isotherms (a) and pore size distribution curves (b)
is N2 adsorption-desorption isotherms of the as-synthesized YS-x zeolite samples obtained from the dried gel precursors with a different SiO2/Al2O3 ratio. The adsorption-desorption of nitrogen on sample YH-5.18 is a type-I isotherm, indicating the presence of micropores only. However, larger hysteresis loops occur in the adsorption-desorption isotherms of the YS-4.14, YS-5.18, YS-6.21 and YS-7.25, indicating the presence of mesopores in the samples obtained by SAC procedure. Combining with the results observed in SEM images mentioned in Fig. 2 and TEM image shown in Fig. 4, the larger hysteresis loops occurring in the isotherms should therefore be attributed to capillary condensation in open mesopores or macropores obtained by filling the primary nanocrystals or polycrystalline aggregates interparticle spaces[
It can be seen from Table 2 that the external surface areas of the as-synthesized hierarchical Y are 41-51 m2/g, which is more than 2 times as much as the 21 m2/g of the reference YH-5.18 zeolite obtained by traditional hydrothermal procedure. The elevated external surface areas can be attributed to the nanocrystallization of primary Y crystalline grains in the sphere-like hierarchical Y. Table 2 also illustrates that the micropore surface area and volume of the sphere-like Y are lower varying degree than 714 m2/g and 0.27 cm3/g of the reference YH-5.18, respectively because of the deteriorated ordering of three-dimensional network of the primary nanocrystals. The aforementioned results indicate that a hierarchical pore system has been introduced into the as-synthesized Y sample, which owns the regular micropores of FAU zeolite structure, and a meso- and macroporous system resulting from the interparticle spaces of nano-sized primary or polycrystalline aggregating Y crystals.
3 Conclusions
Sphere-like hierarchical Y zeolite polycrystalline aggregates consisting of primary crystals were synthesized by a “Steam-Assisted Conversion (SAC)” procedure. Primary or/and subprime building units or crystallites with primary zeolite framework were verified to be created during preparing the dried gel, and the created building units or crystallites induced a burst in nucleation rate, and primary nano-sized zeolite crystals were created that subsequently self-assembly formed sphere-like polycrystalline Y aggregates. The loosely aggregating nancrystallites offer the as-synthesized samples a larger mesopore volume and external surface areas at the cost of less sacrificed micropore volume and micropore area.
References
[1] Z CHEN W, M HAN D, H SUN X. Studies on the preliminary cracking of heavy oils: contributions of various factors. Fuel, 106, 498-504(2013).
[2] V CHOUDHARY T. Structure-reactivity-mechanistic considerations in heavy oil desulfurization. Industrial & Engineering Chemistry Research, 46, 8363-8370(2007).
[3] M BOLTZ, X LIU J, S MITCHELL. Engineering of zsm-5 zeolite crystals for enhanced lifetime in the production of light olefins
[4] F JING Z, H MA Y, D XU D. π-π interaction of aromatic groups in amphiphilic molecules directing for single-crystalline mesostructured zeolite nanosheets. Nature Communications, 5, 4262-4270(2014).
[5] S CHO H, M CHOI, R SRIVASTAVA. Amphiphilic organosilane-directed synthesis of crystalline zeolite with tunable mesoporosity. Nature Materials, 5, 718-723(2006).
[6] T BACH, C GROEN J, U ZIESE. Creation of hollow zeolite architectures by controlled desilication of Al-zoned zsm-5 crystals. Journal of the American Chemical Society, 127, 10792-10793(2005).
[7] C PENG, Y YAN H, L ZHANG J. Synthesis of hierarchical zeolite beta with low organic template content
[8] M JACUBINAS R, K MÖLER, B YILMAZ. One-step synthesis of hierarchical zeolite beta
[9] E BALANZAT, V MAVRODINOVA, V VALTCHEV. High energy ion irradiation-induced ordered macropores in zeolite crystals. Journal of the American Chemical Society, 133, 18950-18956(2011).
[10] Y JI X, H LI S, L XU. Self-assembly of cetyltrimethylammonium bromide and lamellar zeolite precursor for the preparation of hierarchical MWW zeolite. Chemistry of Materials, 28, 4512-4521(2016).
[11] C WANG P, B ZHANG H, Y ZHAO. Tailoring the morphology of MTW zeolite mesocrystals: intertwined classical/nonclassical crystallization. Chemistry of Materials, 29, 3387-3396(2017).
[12] F MEIRER, M WECKHUYSEN B. FIB-SEM tomography probes the mesoscale pore space of an individual catalytic cracking particle. ACS Catalysis, 6, 3158-3167(2016).
[13] J KARGER, P KORTUNOV, S VASENKOV. The role of mesopores in intracrystalline transport in usy zeolite: PFG NMR diffusion study on various length scales. Journal of the American Chemical Society, 127, 13055-13059(2005).
[14] T XU T, F XUE C, J ZHENG J. Silicalite-1 monolith with vertically aligned mesopores templated from carbon nanotube array. Materials Letters, 154, 55-59(2015).
[15] J ZHU, K ZHU L, H ZHU Y. Highly mesoporous single- crystalline zeolite beta synthesized using a nonsurfactant cationic polymer as a dual-function template. Journal of the American Chemical Society, 136, 2503-2510(2014).
[16] C LIU Z, D WANG Y, B ZHU H. Nanosized CaCO3 as hard template for creation of intracrystal pores within silicalite-1 crystal. Chemistry of Materials, 20, 1134-1139(2008).
[17] X DONG J, P LI J, Y XU W. A novel method for the preparation of zeolite ZSM-5.. Journal of the Chemical Society, Chemical Communications, 10, 755-756(1990).
[18] M MATSUKATA, M OGURA, T OSAKI. Conversion of dry gel to microporous crystals in gas phase. Topics in Catalysis, 9, 77-92(1999).
[19] D HU, H LU X, H XIA Q. Synthesis of ultrafine zeolites by dry-gel conversion without any organic additive. Materials Research Bulletin, 43, 3553-3561(2008).
[20] M MATSUKATA, M OGURA, T OSAKI. Quantitative analyses for TEA+ and Na+ contents in zeolite beta with a wide range of Si/Al ratio. Microporous & Mesoporous Materials, 48, 23-29(2001).
[21] S ALFARO, M ARRUEBO, J CORONAS. Preparation of MFI type tubular membranes by steam-assisted crystallization. Microporous & Mesoporous Materials, 50, 195-200(2001).
[22] S BAI, W CHEN Z, J ZHANG. Core-shell zeolite Y with ant-nest like hollow interior constructed by amino acids and enhanced catalytic activity. Journal of Materials Chemistry A, 5, 20757-20764(2017).
[23] Q GUO, B QIN, W ZHANG X. Structural features of binary microporous zeolite composite Y-beta and its hydrocracking performance. Catalysis Today, 149, 212-217(2010).
[24] T CACCIAGUERRA, F DRIOLE M, A MORSLI. Microporosity of the amorphous aluminosilicate precursors of zeolites: the case of the gels of synthesis of mordenite. Microporous & Mesoporous Materials, 104, 209-216(2007).
[25] A PRAMATHA P, R RANI V, R SINGH. Existence of colloidal primitive building units exhibiting memory effects in zeolite growth compositions. Journal of Physical Chemistry B, 108, 20465-20470(2004).
[26] J DEKA, V KARUNAKAR G, L SATYANARAYANA. Chiral modification of copper exchanged zeolite-Y with cinchonidine and its application in the asymmetric Henry reaction.. Dalton Transactions, 44, 20949-20963(2015).

Set citation alerts for the article
Please enter your email address